API Drilling and Mining Use Zirconia Ceramic Pump Fmc 435/420 Liners Mud Pump Liner

• Customization: Available
• After-sales Service: 24/7
• Warranty: 24/7
• Model NO.: GPE-M
• Certification: API
• Power Source: API
• Operation Pressure: Atmospheric Pressure
• Material: Plastic
• Type: Mud Pump
• Volume Density(g/cm3): 3.9
• Bending Strength(MPa): 350
• Young′s Modulus(Gpa): 370
• Specification: PISTON PUMP
• Trademark: GOLDENMAN
• Origin: China
• HS Code: 8431
• Production Capacity: 150000
• Package Size: 90.00cm * 60.00cm * 60.00cm
• Package Gross Weight: 96.000kg

Product Description

Emsco Ideco Bomco GD triplex mud pump liner for oil well

Zirconia Ceramic liner Ceramic Sleeve for pump have exceptional hardness and strength, resistance to chemical attack and wear, low dielectric loss and excellent electrical insulation properties. Additionally, Alumina can be metallized for brazing to other metals, highly polished, and comes in a variety of purities depending on it use. Due to these outstanding properties ceramic Alumina tubes are used in a wide range of industrial and advanced applications.
 

1.Emsco Ideco Bomco GD triplex mud pump liner for oil well combine the strength of a forged steel outer shell with the abrasion
and corrosion reisistance of a high chromium iron inner sleeve.
2.Feature a centrifugally cast high chrome iron sleeve which is machined and heat treated to a minmum uniform bore hardness of
HRC65
3. The surface of Emsco Ideco Bomco GD triplex mud pump liner for oil well with a mirror-like smooth finish and the inner holes'
dimension tolerance is strictly controlled to ensure a long using life of more than 800 hours.
4. Our liner made for superior performance under tough corrosive and abrasive conditions.
We supply all common models of drilling rig mud pump liner in material zirconia ceramic and high chrome bimetal for Emsco, Gardner
Denver, National, Oil well, Continental, Ideco, 3NB series mud pump and so on, ceramic liner inner sleeve material is 99.99%
zirconia, high chrome bimetal liner is forgings , with chrome content 28%, HRC 65.



 

List of Physical Characteristic Parameters of Ceramic Cylinder Sleeves  

Material item	Aluminum oxide	ZTA	Zirconia
Volume density(g/cm^3)	3.9	4.17	6.0
Vickers hardness(GPa)	13	12	11
Bending strength(MPa)	350	480	800
Fracture tenacity(MPa.m^1/2)	4	5	9
Young's modulus(GPa)	370	330	200
Abrasion resistance(min/cm^3)	15	35	40
Linear expansion coefficient(40-800ºC)(×10^-6/ºC)	8.0	8.8	11.0
Roughness(Ra)(μm)	0.3	0.2	0.1
Acid resistant(95%sulfuric acid,95ºC)(WT Loss,mg/cm^2.d)	0.25	0.2	0.04
Alkali resistance(30%caustic sodium,80ºC)(WT Loss,mg/cm^2.d)	0.05	0.06	0.08